GCT3A-PTFE | 3-mil PTFE Glass Cloth Tape with Acrylic Adhesive

Harmonization Code : 7019.59.00.90 |   Glass fibres (including glass wool) and articles thereof (for example, yarn, woven fabrics) : Other woven fabrics : Other : Other
Main features
  • 3-mil PTFE Glass Cloth Tape with Acrylic Adhesive
  • Nonstick Surface
  • Good Chemical Resistance

Product Description

LINQTAPE GCT3A-PTFE-Series Glass Cloth Tape has a brown woven glass cloth backing impregnated with PTFE (polytetrafluoroethylene). This tape provides a slick surface on process machinery and offers an extremely low coefficient of friction which, in combination with a pressure sensitive adhesive, creates a non-stick surface that performs at elevated temperatures. This tape can be supplied with or without liner.

Applications:

  • Non-stick surface for paints
  • Heat-sealing machine
  • Conveyor Belts
  • Thermal Insulation
Product Family
GCT3A-PTFE-Series  
25.4 mm
33 m

Coming Soon

This product is currently under development. We are working to get it available online as soon as possible. Please contact us for information on current project status.

Technical Specifications

General Properties
Adhesive Layer
Adhesive Layer
A layer that is applied to one surface or both to bind items together and resist their separation
Acrylic
Adhesive Thickness
Adhesive Thickness
Adhesive thickness indicates the thickness of an adhesive layer.

It refers to the adhesive thickness of a single side so for double sided tapes it always needs to be multiplied.
50.8 µm
Chemistry Type Glass Cloth
Color
Color
The color
Brown
Film Thickness
Film Thickness
Film thickness is the thickness of a backing film without taking into account any coatings or adhesive layers. It is measured in micron and the conversion factor to mil is 0.039.
76.2 µm
Release Liner
Release Liner
A paper or plastic-based film sheet used to prevent a sticky surface from prematurely adhering
No
Single or Double-Sided Adhesive
Single or Double-Sided Adhesive
Describes whether a tape is single- or double-sided. If it is single-sided, it has adhesive only on one side of the backing film. If it is double-sided, then it has adhesive on both sides of the backing film.
Single-Sided
Total Thickness
Total Thickness
Total thickness is taking into account all the films, coatings, adhesives, release liners and special layers and is the maximum thickness of a film or tape.
127 μm
Mechanical Properties
Adhesion Strength
Adhesion Strength
Adhesion is the bond strength measurement of a coating to a substrate. When an adhesive is bonded to an item or surface, numerous physical, mechanical and chemical forces come into play, which may have an effect on each other.
30 Oz/in
Elongation
Elongation
Elongation is the process of lengthening something.

It is a percentage that measures the initial, unstressed, length compared to the length of the material right before it breaks.

It is commonly referred to as Ultimate Elongation or Tensile Elongation at break.
5 %
Tensile Strength (Thin Film)
Tensile Strength (Thin Film)
Tensile strength determines the resistance of a material to break under tension and it measures how much elongating load (or tensile stress) it can handle before fracture.

To make it simple, it measures how much force we have to apply when pulling apart a material before it breaks.
177 N/cm
Electrical Properties
Dielectric Strength
Dielectric Strength
Dielectric strength is measured in kV per mm and is calculated by the Breakdown voltage divided by the thickness of the tested material.

Those two properties go hand in hand and while Breakdown voltage is always thickness dependent, dielectric strength is a general material property.

As an example, the dielectric strength of Polyimide is 236 kV/mm. If we place 1mm of Polyimide between two electrodes, it will act as an insulator until the voltage between the electrodes reaches 236 kV. At this point it will start acting as a good conductor, causing sparks, potential punctures and current flow.
94 kV/mm
Thermal Properties
Temperature Resistance
Temperature Resistance
Temperature resistance is the maximum temperature that the material or product can withstand for a period of time.

The temperatures listed should be considered as guidelines for an operating temperature of about 30 minutes. Typically, the material can withstand much longer times at temperatures about 20°C lower and can withstand much higher temperatures for short, intermittent times.
155 ˚C