Anhydride Cured Epoxy Molding Compounds

Semiconductor & industrial grade epoxy molding compounds

Ask CAPLINQ. Epoxy Mold Compound Experts.

Anhydride-cured Epoxy Mold Compounds

Epoxy Molding Compounds basic building blocks are made of the following ingredients:

  • Epoxy Resin
  • Epoxy Curing Agent (often referred to as Epoxy Hardener)
  • Catalyst
  • Filler
  • Pigment
  • Additives

The choice of curing agent or hardener is an important one, and gives Epoxy Molding Compound very specific material properties once cured (the process of hardening).

The definition of an anhydride is the compound obtained by removing the elements of water from a particular acid, an organic compound containing the group —C(O)OC(O)—, derived from a carboxylic acid. For our purpose, however, it's important to know that epoxy molding compounds generally have unique properties once cured.

The unique benefits offered by anhydride epoxy molding compounds

  • Low mix viscosities for long flow molding
  • Excellent electrical insulation properties
  • Low ionic movement at elevated temperatures (leading to very stable electrical properties at higher temperatures
  • Very good temperature stability, leading to longer shelf life and pot life
  • Good mechanical properties
  • Outstanding thermal endurance

Many types of Anhydride Curing Agents for Epoxies

Although "Anhydride-Cured Epoxy Molding Compounds" properly defines a subcategory of Epoxy Mold Compounds, within this category there is still a wide range of anhydrides one can choose from, and the industry is always developing new types. Among these choices are:

  • Aromatic anhydrides
  • Alicyclic anhydrides
  • Aliphatic anhydrides

Each of which offer further unique material properties. For now, suffice it to say that Anhydride cured Epoxy Molding Compounds offer unique benefits. If you would like to learn more about anhydrides used in epoxy molding compounds, you are welcomed to continue reading in the Learn More about Anhydride-cured Epoxy Mold Compounds section below.

Read More about Anhydride-cured Epoxy Mold Compounds

Product Selector Guide

Anhydride cured epoxy molding compounds
Product
Part#
Product
Description
Key Mechanical Properties
Specific
Gravity
Glass Transition
Temperature (Tg), °C
CTE, Alpha 1
ppm/°C
CTE, Alpha 2
ppm/°C
Flexural Modulus
@25°C
GPa
Flexural Strength
@25°C
MPa
Spiral Flow
@150°C
inches
Gel Time
@160°C
seconds
Top of Page
CAPLINQ Product Selector Guide and Property Overview of Anhydride-based Epoxy Molding Compounds
LinqSol® is a registered trademark of CAPLINQ Corporation
MH6-0330 Black For bushing, high voltage applications requiring excellent electrical insulation and large (up to 5kg) mold shot 1.86 105°C TBD TBD 13.8 138 15 28
MH6-0504 Black Solenoid coils (coil winded fluid valves), power/current transformer, relays, switches 2.15 140°C 42 118 13.5 148 30 22
MH6-0508NF Black "NF” to signify it is non-flameout version (per UL94-V0) of Mh6-0504 1.93 TBD TBD TBD TBD TBD TBD TBD
MH6-0510 Green Green color version of MH6-0504 Black TBD 140°C 41 112 14.6 145 TBD TBD

Frequently Asked Questions

Frequently Asked Questions about Anhydride-Cured Epoxies

Don't anhydride-cured epoxies have a low Tg?

Not anymore. It has historically been true that anhydride-cured epoxies had a glass transition temperature (Tg) that was lower than 150°C. Modern-day epoxies using an ahydride curing agent can have Tgs above 200°C.

Are there any downsides to anhydride curing agents?

Yes. The biggest downside to anhydride-cured epoxies these days is the high moistire absorption during cure. Epoxy cresol novolacs are other phenolic-based curing agents have moisture absorptions that are lower than those obtained with anhydrides. For large devices requiring high MSL performance, this can be an issue still, but for discrete through hole devices, this should not be an issue.


Learn More

Anhydride chemistry still has a bright future for epoxy mold compound formulations

In a world of more stringent environmental controls and ever hotter operating temperatures for epoxy mold compounds are getting a bad reputation. This reputation is not only misplaced, it often misses the point completely.

Anhydride curing agents are some of epoxies oldest curing agents, and probably the most widely used curing agent in epoxy molding compounds’ 75+ year history. This is not a coincidence. Although epoxy molding compound chemistry has evolved over these same 75 years into novolacs, phenolics, bismaleimides, and multi-aromatic resins, anhydride chemistry still holds an important place not only in history but in the future as well. This section will concede that the use of anhydride epoxy mold compounds may be sunsetting for some applications, but for a wide range of other applications, it may still be the best choice.

In order to talk about the future of anhydride chemistries, it’s important to highlight some of anhydrides known myths, and what exactly the future holds for these:

  • Anhydrides contain ingredients on the SVHC list
  • Anhydrides cannot be used in higher-temperature applications
  • Anhydrides tend to have higher moisture absorption than other chemistries
  • Anhydrides have CTE’s that are too high for modern-day applications

Concern 1: Anhydride chemistry contains ingredients on the SVHC list

The Substances of Very High Concern or SVHC list is a list of chemicals (substances) created by the European CHemicals Agency (ECHA) to record substances that have been tested deemed to be either:

  • Persistent, bioaccumulative and toxic
  • Toxic for reproduction or
  • Carcinogenic (cancer causing)

Since 2012, only two anhydrides have made it on this list, and since there are many different types and formulations of anhydrides to choose from, these two hardly make up the majority of anhydride formulations available to use in an epoxy mold compound formulation.

Furthermore, new developments and research continues, and these have identified many new types of anhydride formulations that are quite different than these types of anhydrides and aren’t expected to ever make it onto the ECHA SVHC list.

This said, it’s important to point out that anhydrides are hardly a black sheep in this respect. Simply by not using anhydrides in epoxy mold compound formulations does not preclude it from having substances that will end up on the SVHC list. Many other types of epoxy formulation chemistries including multi-aromatic resins, bismaleimides, novolacs, and phenolics have used substances that have also found their way onto the SVHC list.

Concern 2: Anhydrides cannot be used in higher temperature applications

Let’s first define what “higher temperature applications” actually are and then we can discuss the suitability of epoxy molding compounds for these applications. While yes, it is true that automotive applications see a trend to temperatures that approach 220°C or even 250°C over the next 10-15 years, these are still the upper temperatures of such applications. The majority of applications that use epoxy mold compounds still see 180C as well above the application operating temperature.

Table 1. UL-Approved Electrical Insulation system (EIS) Class
Maximum
temperature at hottest spot
UL 1446
temperature classes
IEC85 temperature classes
- - Y
- - A
- - E
130°C (266°F) B B
155°C (311°F) F F
180°C (356°F) H H
200°C (392°F) N 200
220°C (428°F) R 220
240°C (464°F) S 250
over 240°C (over 464°F) >240°C *
*Above 250°C, each class is a temperature of 25°C higher than the preceding one. (ie. 275, 300, etc.)

To add insult to injury, engineers often mistake a material’s glass transition temperature (Tg) for its maximum operating temperature. While it is true that a materials’ physical properties - including its coefficient of thermal expansion (CTE) and Flexural Modulus (E) – do change at a material’s Tg, these are not signs of material degradation. In many cases, these properties go through a perfect hysteresis meaning that the material’s original CTE and modulus are reverted once the temperature is returned below its Tg.

But don’t take our word for it, the proof is in the pudding as they say. The Underwriter’s Laboratory (UL) has designed a UL-Approved Electrical Insulation system (EIS) class which are based on the maximum "hot spot" in the system. (See Table 1) .

Manufacturers have been formulating two anhydride chemistries, MH6-0504 and MH6-0510 for over forty years that are in use on applications that have a Class H rating, meaning they can be used in applications that can see temperatures up to 180°C.

In addition to this, though anhydride chemistries may not be able to achieve the same higher maximum electrical insulation class (Class N) as some of its novolac counterparts, the temperatures at which it is stable (up to 180C), it is very stable.

As you can see in Figure 1 below, test were carried out with a “green color” version of epoxy molding compounds in both an anhydride chemistry and a novolac chemistry. The green colored novolac chemistry candidate showed a much worse temperature stability than the same color mold compound using an anhydride chemistry.

Anhydride chemistry is much more color stable at 180°C then novolac chemistry Figure 1: Anhydride chemistry is much more color stable at 180°C then novolac chemistry

Concern 3: Anhydrides have a higher moisture absorption than other chemistries

Moisture absorption tests measure the amount of moisture that epoxy mold compounds absorb after post mold curing and exposed to high moisture environments. Three standard tests for this include:

  • 1 hour water boil @ 100°C
  • 24 hour water soak @ 23°C
  • 168 hour moisture exposure at 85°C and 85% relative humidity (RH)

In all three of these tests, anhydride chemistries have a distinct disadvantage against other epoxy mold compound chemistries. They all reveal that the moisture absorption of anhydride chemistries is greater than their counterparts. So why does this matter to us?

A significant amount of epoxy mold compounds are used in the manufacture of semiconductor devices. In semiconductor applications, epoxy is used to encapsulate the semiconductor chip, thus providing both mechanical and environmental protection.

Early in the development of epoxy mold compounds for semiconductors, Joint Electron Device Engineering Council (JEDEC), an independent semiconductor engineering trade organization and standardization body, developed a series of moisture sensitivity level (MSL) tests that correlated the MSL level of semiconductor devices to the floor life of these same devices before these same devices needed to be “prebaked” again. See Table 2.

Table 2. JEDEC Moisture Sensitivity Level (MSL)
Soak Requirements
Floor Life Standard Accelerated
Level Time Condition
°C/%RH
Time (hrs) Cond
°C/%RH
Time (hrs) Condition
°C/%RH
1 unlimited <=30°C/85%RH 168+5/-0 85°C/85%RH n/a n/a
2 1 year <=30°C/60%RH 168+5/-0 85°C/60%RH n/a n/a
2a 4 weeks <=30°C/60%RH 696+5/-0 30°C/60%RH 120+1/-0 60°C/60%RH
3 168 hours <=30°C/60%RH 192+5/-0 30°C/60%RH 40+1/-0 60°C/60%RH
4 72 hours <=30°C/60%RH 96+2/-0 30°C/60%RH 20+0.5/-0 60°C/60%RH
5 48 hours <=30°C/60%RH 72+2/-0 30°C/60%RH 15+0.5/-0 60°C/60%RH
5a 24 hours <=30°C/60%RH 48+2/-0 30°C/60%RH 10+0.5/-0 60°C/60%RH
6 TOL <=30°C/60%RH TOL 30°C/60%RH n/a 60°C/60%RH
1. TOL means 'Time on Label', or the time indicated on the label of the packing.
2. The standard soak time is the sum of the default value of 24H for the semiconductor manufacturer's exposure time (MET) between bake and bag and the floor life or maximum time allowed out of the bag at the end user or distributor's facility. For example, an MSL 3 package will require a standard soak time of 192 hours, which is 168 hours of floor life plus 24 hours between bake and bag at the semiconductor manufacturer.

“Prebaking” is a process in the printed circuit board (PCB) assembly process that literally bakes the semiconductor devices in an oven for 24 hours @ 100°C to drive out moisture that may have accumulated in the device as the device sat on the production floor waiting to be mounted onto the printed circuit board.

Because the printed circuit board process always involves the soldering of components onto the PCB in a solder reflow oven, a process that exposes the PCB and all its components to temperatures up to 260°C for up to 10 minutes, it is critical that all the components can withstand this temperature cycle.

What was discovered was that in the absence of this prebaking step, semiconductor devices that contained too much moisture would fail catastrophically during this reflow step as moisture trapped within the epoxy mold compound would expand and cause delamination from the semiconductor device, break critical wirebonds and separate from the leadframe in a process now coined “popcorning”.

MSL tests are very useful for PCB manufacturers as it gives them a common guideline they can adopt for their semiconductor device suppliers. For epoxy mold compound manufacturers, on the other hand, the criteria is more abstract as the semiconductor devices range wildly in size, shape, and materials used.

There are literally thousands of different combinations when one considers all the potential variables – a number that has only increased in modern times as devices types and materials continue to evolve.

Fortunately for epoxy mold compound manufacturers, there are three main material properties that will indicate whether an encapsulant will have better MSL performance than its predecessor or competitor:

  • Higher adhesion to the given substrates
  • A matched coefficient of thermal expansion (CTE)
  • A lower moisture absorption

A higher adhesion to the substrate is logical as an unbroken bond will not fail, and the matched CTE will be discussed more in the next section, but the last point brings us full circle on our discussion of the importance of low moisture absorption.

So what happens if there is no high-temperature solder reflow step, as there weren’t in discrete, through-hole components or in other, non-semiconductor applications? Then moisture absorption values become less relevant, and the whole concern over “higher moisture absorption” of anhydride chemistries no longer holds water, as a humorous chemist may say.

Concern 4: Anhydrides’ CTE’s are too high for modern-day applications

As explained in the section above, it is important for semiconductor device manufacturers using epoxy molding compounds to select encapsulants that “match” the coefficient of thermal expansion of their leadframes and substrates. Refer to Table 3 for the list of typical material used in the semiconductor industry.

Material Coefficient of Thermal Expansion (CTE), ppm/°C Silicon 3 ppm/°C Ceramic 6.7 ppm/°C Al2O3 Ceramic Substrate* *High Thermal Conductivity for Direct Bond Copper (DBC) for Power Modules 7-8 ppm/°C PCB, FR4 Laminate 14-17 ppm/°C Copper (Cu) 17 ppm/°C Silver (Ag) 18 ppm/°C

The reason this is so critical in semiconductor devices manufacturing is that the dimensions are so tiny (measured in microns and nanometers) and the stresses caused by the high-temperature solder reflow process are so high, that even the slightest CTE mismatch can cause catastrophic semiconductor device failure.

This phenomenon has only been exaggerated over the past decade as semiconductor devices have gotten even smaller, manufacturers have moved to even higher temperature reflow profiles to accommodate lead-free solders and PCB assemblers have insisted on ever-higher MSL performance.