LOCTITE ABLESTIK 84-1LMIS

Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other

Main features

Long work life
Solvent free
Electrically conductive

Product Description

LOCTITE ABLESTIK 84-1LMIS epoxy adhesive is designed for semiconductor packaging applications. This adhesive is ideal for application by dispensing or stamping.

LOCTITE ABLESTIK 84-1LMIS is a silver coloured, electrically conductive solvent free adhesive with a long work life, typically used in die attach applications.

Cure Schedule

1 hour @ 175°C
30 minutes @ 200°C

Specifications

Technical Specifications

General Properties

Shelf Life Shelf Life Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties. It differs vastly per product and it is based on temperature and storage conditions. The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ -40°C	365 days

Work life @25°C

Work life @25°C
Work life is the amount of time we have to work with a material until it is no longer able to be easily worked and applied on a substrate.

It is based on the change in viscosity and it can rely on the application requirements.

96 hours

Chemical Properties

Ionic Content
Chloride (Cl-) Chloride (Cl-) The amount of Chloride (Cl-) ion extracted from the product in parts per million (ppm)	10 ppm
Potassium (K+) Potassium (K+) The amount of Potassium (K+) ion extracted from the product in parts per million (ppm)	5 ppm
Sodium (Na+) Sodium (Na+) The amount of Sodium (Na+) ion extracted from the product in parts per million (ppm)	10 ppm

Mechanical Properties

Shear strength
Shear Strength @25°C	12.9 N/mm2

Viscosity Viscosity Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application
Thixotropic index Thixotropic index Thixotropic Index is a ratio of a material s viscosity at two different speeds in Ambient temperature, generally different by a factor of ten. A thixotropic material s viscosity will decrease as agitation or pressure is increased. It indicates the capability of a material to hold its shape. Mayonnaise is a great example of this. It holds its shape very well, but when a shear stress is applied, the material easily spreads. It helps in choosing a material in accordance to the application, dispense method and viscosity of a material.	4.0
Viscosity	17,000 mPa.s

Electrical Properties

Volume Resistivity

Volume Resistivity
Volume resistivity, also called volume resistance, bulk resistance or bulk resistivity is a thickness dependent measurement of the resistivity of a material perpendicular to the plane of the surface.

2.0x10^-4 Ohms⋅cm

Thermal Properties

Coefficient of Thermal Expansion (CTE) Coefficient of Thermal Expansion (CTE) CTE (Coefficient of thermal expansion) is a material property that is indicative of the extent to which a material expands with a change in temperature. This can be a change in length, area or volume, depending on the material. Knowing the CTE of the layers is helpful in analyzing stresses that might occur when a system consists of an adhesive plus some other solid component.
Coefficient of Thermal Expansion (CTE), α1 Coefficient of Thermal Expansion (CTE), α1 CTE α1 (alpha 1) is the slope of the Coefficient of thermal expansion in a temperature range below the Glass transition temperature (Tg). It explains how much a material will expand until it reaches Tg.	46 ppm/°C
Coefficient of Thermal Expansion (CTE), α2 Coefficient of Thermal Expansion (CTE), α2 CTE α2 (alpha 2) is the slope of the Coefficient of thermal expansion in a temperature range above the Glass transition temperature (Tg). It explains the extent to which a material will expand after it passes Tg.	246 ppm/°C

Glass Transition Temperature (Tg)

Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.

127 °C

Thermal Conductivity

Thermal Conductivity
Thermal conductivity describes the ability of a material to conduct heat. It is required by power packages in order to dissipate heat and maintain stable electrical performance.

Thermal conductivity units are [W/(m K)] in the SI system and [Btu/(hr ft °F)] in the Imperial system.

1.5 W/m.K