LOCTITE ECCOBOND UF 3810

Harmonization Code : 3907.30.00.90 | Polyacetals, other polyethers and epoxide resins, in primary forms; polycarbonates, alkyd resins, polyallyl esters and other polyesters, in primary forms : Epoxide resins : Other

Main features

High Tg
Halogen free
Reworkable

Product Description

LOCTITE® ECCOBOND UF 3810 reworkable, epoxy underfill is designed for CSP and BGA applications. It has high Tg and has stable electrical performance in temperature himidity bias. This material cures quickly at moderate temperatures to minimize stress to other components. When cured, it provides excellent mechanical properties to protect solder joints during thermal cycling.

LOCTITE® ECCOBOND UF 3810 is a single component, halogen free black material, compatible with most Pb-free solders. It can flow in temperature and cure fast at moderate temperatures.

Cure Schedule

≥8 minutes @ 130°C

Specifications

Technical Specifications

General Properties

Shelf Life Shelf Life Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties. It differs vastly per product and it is based on temperature and storage conditions. The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ -20°C	365 days

Specific Gravity

Specific Gravity
Specific gravity (SG) is the ratio of the density of a substance to the density of a reference substance; equivalently, it is the ratio of the mass of a substance to the mass of a reference substance for the same given volume.

For liquids, the reference substance is almost always water (1), while for gases, it is air (1.18) at room temperature. Specific gravity is unitless.

1.13

Physical Properties

Viscosity

Viscosity
Viscosity is a measurement of a fluid’s resistance to flow.

Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.

A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
water would.

The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application

394 mPa.s

Chemical Properties

Ionic Content
Chloride (Cl-) Chloride (Cl-) The amount of Chloride (Cl-) ion extracted from the product in parts per million (ppm)	0.8 ppm
Sodium (Na+) Sodium (Na+) The amount of Sodium (Na+) ion extracted from the product in parts per million (ppm)	0.7 ppm

Mechanical Properties

Storage (DMA) Modulus
Storage (DMA) Modulus @ -65°C	3,820 N/mm2
Storage (DMA) Modulus @ 100°C	850 N/mm2
Storage (DMA) Modulus @ 200°C	30 N/mm2
Storage (DMA) Modulus @ 25°C	2,990 N/mm2

Thermal Properties

Coefficient of Thermal Expansion (CTE) Coefficient of Thermal Expansion (CTE) CTE (Coefficient of thermal expansion) is a material property that is indicative of the extent to which a material expands with a change in temperature. This can be a change in length, area or volume, depending on the material. Knowing the CTE of the layers is helpful in analyzing stresses that might occur when a system consists of an adhesive plus some other solid component.
Coefficient of Thermal Expansion (CTE), α1 Coefficient of Thermal Expansion (CTE), α1 CTE α1 (alpha 1) is the slope of the Coefficient of thermal expansion in a temperature range below the Glass transition temperature (Tg). It explains how much a material will expand until it reaches Tg.	55 ppm/°C
Coefficient of Thermal Expansion (CTE), α2 Coefficient of Thermal Expansion (CTE), α2 CTE α2 (alpha 2) is the slope of the Coefficient of thermal expansion in a temperature range above the Glass transition temperature (Tg). It explains the extent to which a material will expand after it passes Tg.	171 ppm/°C

Glass Transition Temperature (Tg)

Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.

102 °C