LOCTITE ECCOBOND UV8800M-X

Harmonization Code : 3907.30.00.90 | Polyacetals, other polyethers and epoxide resins, in primary forms; polycarbonates, alkyd resins, polyallyl esters and other polyesters, in primary forms : Epoxide resins : Other

Main features

Fast UV Cure
Good workability
Good adhesion

Product Description

LOCTITE ECCOBOND UV8800M-X encapsulant is formulated for use in smart card applications. It cures to form a hard translucent coating when exposed to UV light of sufficient intensity. The curing of the product is not inhibited by oxygen, resulting in excellent surface cure.

LOCTITE ECCOBOND UV8800M-X glob top encapsulant can be used on FR4, FCI and LG tape substrates.

Typical UV Cure Condition

Light Intensity, mW/cm2 100
Exposure Time, seconds 30

Product Family
UV8800M-X

1. Select Package Type

1Kg Bottle

Catalog Product

Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.

Shortest leadtime

Not Available

Shipping in 8 - 12 weeks

Contact for Pricing

Packaging

TDS & SDS

Compare product

Specifications

Technical Specifications

General Properties

Shelf Life Shelf Life Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties. It differs vastly per product and it is based on temperature and storage conditions. The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ 5°C	180 days

Chemical Properties

Extractable Ionic Content, after 20 hours
Chloride (Cl-) Chloride (Cl-) The amount of Chloride (Cl-) ion extracted from the product in parts per million (ppm)	10 ppm
Sodium (Na+) Sodium (Na+) The amount of Sodium (Na+) ion extracted from the product in parts per million (ppm)	10 ppm

Mechanical Properties

Viscosity Viscosity Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application
Viscosity	3,400 mPa.s
Thixotropic index Thixotropic index Thixotropic Index is a ratio of a material s viscosity at two different speeds in Ambient temperature, generally different by a factor of ten. A thixotropic material s viscosity will decrease as agitation or pressure is increased. It indicates the capability of a material to hold its shape. Mayonnaise is a great example of this. It holds its shape very well, but when a shear stress is applied, the material easily spreads. It helps in choosing a material in accordance to the application, dispense method and viscosity of a material.	1.1

Storage (DMA) Modulus
Storage (DMA) Modulus @ 25°C	4,816 N/mm2
Storage (DMA) Modulus @ 100°C	94 N/mm2
Storage (DMA) Modulus @ 200°C	63 N/mm2

Hardness Hardness Hardness is a dimensionless quantity. There is no direct relationship between measurements in one scale and their equivalent in another scale or another hardness test.
Durometer (Shore D)	80

Thermal Properties

Glass Transition Temperature (Tg)

Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.

47 °C

Coefficient of Thermal Expansion (CTE) Coefficient of Thermal Expansion (CTE) CTE (Coefficient of thermal expansion) is a material property that is indicative of the extent to which a material expands with a change in temperature. This can be a change in length, area or volume, depending on the material. Knowing the CTE of the layers is helpful in analyzing stresses that might occur when a system consists of an adhesive plus some other solid component.
Coefficient of Thermal Expansion (CTE), α1 Coefficient of Thermal Expansion (CTE), α1 CTE α1 (alpha 1) is the slope of the Coefficient of thermal expansion in a temperature range below the Glass transition temperature (Tg). It explains how much a material will expand until it reaches Tg.	48 ppm/°C
Coefficient of Thermal Expansion (CTE), α2 Coefficient of Thermal Expansion (CTE), α2 CTE α2 (alpha 2) is the slope of the Coefficient of thermal expansion in a temperature range above the Glass transition temperature (Tg). It explains the extent to which a material will expand after it passes Tg.	149 ppm/°C