- 3M™ Scotch-Weld™ Epoxy Adhesive DP125
3M™ Scotch-Weld™ Epoxy Adhesive DP125
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- 25-minute worklife
- Flexible
- High peel and shear strength
Product Description
3M™ Scotch-Weld™ Epoxy Adhesive DP125 (Translucent & Gray) is a two-part structural adhesive engineered for fast curing while maintaining excellent strength and flexibility. As a quicker-curing alternative to 3M™ Scotch-Weld™ Epoxy Adhesive 2216 Translucent B/A, it significantly reduces worklife and cure time from hours or days to minutes and hours—without compromising shear and peel performance. The Gray version is a filled, pigmented variant offering similar flexibility and mechanical properties.
Product Key Features
- 25 minute worklife
- Flexible
- High peel and shear strength
- 1:1 mix ratio
Technical Specifications
| Physical Properties | |||||
|
Viscosity
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application |
2000 - 8000 mPa.s | ||||
| General Properties | |||||
|
Color
Color
The color |
Translucent | ||||
|
Mix Ratio
Mix Ratio
The amount of a constituent divided by the total amount of all other constituents in a mixture |
1:1 | ||||
|
Work life @25°C
Work life @25°C
Work life is the amount of time we have to work with a material until it is no longer able to be easily worked and applied on a substrate. It is based on the change in viscosity and it can rely on the application requirements. |
0.42 hours | ||||
| Mechanical Properties | |||||
|
|||||
|
Elongation
Elongation
Elongation is the process of lengthening something. It is a percentage that measures the initial, unstressed, length compared to the length of the material right before it breaks. It is commonly referred to as Ultimate Elongation or Tensile Elongation at break. |
150 % | ||||
|
|||||
| Curing Conditions | |||||
|
|||||