Hydroxyl Functional Adhesion Promoter

Harmonization Code : 2901.10.00.00 |   Acyclic hydrocarbons; Saturated
Main features
  • Enhances the adhesive capabilities of a metal surface
  • 2-4 nm thickness
  • Can be used as an additive

Product Description

Aculon, a proven supplier of industrial-grade coatings, introduces their patented Hydroxyl Functional Adhesion Promoter. Aculon's Hydroxyl Functional Adhesion Promoter is a nano-scale surface treatment coating that promotes adhesion across a broad spectrum of metal surfaces. It is quick and easy to apply and will eliminate adhesive failures.

The adhesion primer can be applied via most traditional coating processes, including dipping, spraying, wiping, etc., and provides an optically clear, uniform coating thickness of 2-4 nm. Also, their actives can be blended into existing formulations for increased surface adhesion of coatings and adhesives. The Hydroxyl Functional Adhesion Promoter is designed to improve adhesion for coatings that cross-link with hydroxyl functional groups, for example, urethane, melamine-formaldehyde, and phenolic-epoxy based coatings.

 

Advantages of Aculon's Hydroxyl Functional Adhesion Promoter

  • Improved adhesion strength of paints/coatings on
    metal surfaces
  • Uniform Thicknesses at the Nanoscale
  • 100% transmission for Visible Light
  • Minimal Capital Equipment Requirements
  • Does not leach
Product Family
Hydroxyl Functional Adhesion Promoter-Series  

Catalog Product

Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.
Packaging
TDS, SDS & Technical documents

Technical Specifications

General Properties
Appearance
Appearance
Appearance at room temperature.
 Off White Powder
Solids 98 %
Shelf Life
Shelf Life
Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties.

It differs vastly per product and it is based on temperature and storage conditions.

The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ 15°C 24 months
Electrical Properties
Visible Light Transmission 100 %
Thermal Properties
Melting Temperature
Melting temperature 110 °C
Other Properties
Coating Thickness 2-4 nm

Additional Information

How to apply the Hydroxyl Functional Adhesion Promoter

STEP 1 ⇨ CLEAN

STEP 2 ⇨ TREAT

STEP 3 ⇨ DRY

Parts must be sufficiently clean before treatment for proper bonding and effective application.

To clean, solvents or soap and water can be used to degrease the substrate.

 

 Spray - Spray the solution onto the substrate using double passes. 

If curing is necessary (short dip times are used), the treated substrates are best cured at 120⁰C peak metal temperature for approximately 30 seconds.

For silicon and titanium oxides, lengthening the cure time
to 5 minutes is recommended.

 

Dip - Fully immerse the part in the treatment solution for 5 minutes. To decrease the dip time, post-cure is recommended for optimal performance.

Dip with Sonification - Completely submerge the substrate in the solution and sonicate for five minutes. Then remove the substrate and allow it to air dry.

 

 

Application Tips

  • For spray application, post-application curing is recommended for best performance. 
  • Coat the substrate as soon as possible after cleaning to prevent recontamination.
  • Spray Equipment Suggestions: HVLP(Binks Mach 1), HVLP(Devilbiss JGHV), Air Atomization(Devilbiss MBC gun), and Airless(Graco Model 225-292 President Pump Series A). 
  • Cure temperatures and conditions should be optimized based on substrate and durability requirements.
  • Clean all equipment with alcohol (e.g., Isopropanol) or the solvent used.
  • If a UV-curable coating system is being used, then it may be necessary to modify the curing parameters to ensure sufficient radical generation near the surface of the monolayer to achieve optimal adhesion.

 

Application Ideas

  • Use to improve lead-frame adhesion in many electronics applications
  • Improved bonding of an epoxy over-mold compound  (best for molding compounds that require a thermal cure above 60-70 ⁰C)
  • Prevent delamination of finished products
  • Increase polyurethane-to-metal adhesion

  • For coatings that cross-link with acrylic functional groups, Methacrylate Functional Adhesion Promoter is a better fit.