LOCTITE EDAG PF 410 E&C
- Screen printable
- Excellent print definition
- Silver filled
LOCTITE EDAG PF 410 E&C is designed for production of flexible circuitry. This material can be used on a variety of substrates and is applicable with manual, semi automatic or high speed reel to reel screen printing equipment.
LOCTITE EDAG PF 410 E&C is passed over a triple roll mill to remove small particles. It offers extended screen residence time and excellent print definition with superior adhesion to polyester film.
- 30 minutes @ 80°C or
- 15 minutes @ 120°C
LOCTITE EDAG PF 410 E&C can be dried immediately after printing at temperatures between 80 to 140°C
| Viscosity |
Viscosity is a measurement of a fluid’s resistance to flow.
Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.
A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application
Optimal Storage : 5 to 30 °C
TYPICAL SCREEN PRINTING PROCESS
-Applied dry coating thickness , μm 8 to 12
-Emulsion Thickness , μm 20 to 40
-Polyurethane , durometer 70 to 75
Recommended Screen Type
-Monofilament polyester screen, threads/cm 68 to 110
-Stainless steel screen , threads/cm 90 to 154
Printing Equipment Type
-High speed reel-to-reel