Aculon Nanoproof 3-002

Harmonization Code : 2901.10.00.00 |   Acyclic hydrocarbons; Saturated
Main features
  • 0.2% Fluoroacrylate Solids
  • 0.1 - 1 um Thickness
  • 3M Novec 1702 replacement

Product Description

Aculon Nanoproof 3-002 is a highly effective electronic coating series designed to provide superior protection against moisture, chemicals, and corrosion for a wide range of electronic applications. With the discontinuation of the popular 3M Novec product line, the Aculon Nanoproof 3.0 series offers a readily available and accessible alternative for industries that require robust protection for their electronic devices.

Aculon Nanoproof 3-002 with 0.2% Fluoroacrylate solids, forms a thin, transparent layer that provides excellent anti-wetting and anti-stiction properties, protecting electronic devices from harmful elements. With this amount of solids, it manages to reach a coating thickness of 0.1 - 1um. The coating also offers electrical insulation properties (3600V/mil Dielectric Strength), reducing the risk of electrical shorts and failures of PCBs and Electrical components.

The Aculon Nanoproof 3.0 series comes in different grades, with Aculon Nanoproof 3-002 offering similar performance and chemical properties to the 3M Novec 1702 product. It is ideal for use in harsh environments, making it a popular choice in industries such as automotive, aerospace, and defense. Aculon Nanoproof 3-002 is easy to apply, and its transparent coating ensures that it does not interfere with the aesthetics or functionality of electronic devices. It is suitable for use on a variety of electronic applications, including printed circuit boards, sensors, switches, and connectors.

Product Family
NNPRF3-002  
20kg Pail 1 Gal Bottle 1 liter Bottle 40ml sample

Catalog Product

Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.

Technical Specifications

General Properties
Appearance
Appearance
Appearance at room temperature.
Light Green
Refractive index
Refractive index
The refractive index determines how much the path of light is bent, or refracted, when entering a material. It is calculated by taking into account the velocity of light in vacuum compared to the velocity of light in the material.

The refractive index calculation can be affected by the wavelength of light and the temperature of the material. Even though it is usually reported on standard wavelengths it is advised to check the TDS for the precise test parameters.
1.376
Solids Fluoroacrylate 0.2 %
Physical Properties
Viscosity
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow.

Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.

A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
water would.

The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application
20 mPa.s
Electrical Properties
Dielectric Strength
Dielectric Strength
Dielectric strength is measured in kV per mm and is calculated by the Breakdown voltage divided by the thickness of the tested material.

Those two properties go hand in hand and while Breakdown voltage is always thickness dependent, dielectric strength is a general material property.

As an example, the dielectric strength of Polyimide is 236 kV/mm. If we place 1mm of Polyimide between two electrodes, it will act as an insulator until the voltage between the electrodes reaches 236 kV. At this point it will start acting as a good conductor, causing sparks, potential punctures and current flow.
3600 kV/mm
Thermal Properties
Glass Transition Temperature (Tg)
Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.
95 °C
Other Properties
Oil Contact Angle
Oil Contact Angle
The contact angle is the angle, conventionally measure trough the liquid, where a liquid-vapor interface meets a solid surface.
80 °
Water Contact Angle 120 °

Additional Information

Thickness depends on the amount of Solids. The higher the amount of solids, the thicker the coating after the solvent evaporates.

 

Aculon Nanoproof 3-002 vs 3M Novec 1702

  3M Novec 1702 Aculon Nanoproof 3-002
Solids Fluoroacrylate 0.2% Fluoroacrylate 0.2%
Solvent 7100DL 347
Appearance Clear Light Green
Density 1.5 g/ml 1.5 g/ml
Viscosity 0.63 cP <20 cP
Boiling point 61°C 56°C
Environmental Non ozone depleting, low in toxocity, low in GWP, RoHS compliant and VOC exempt per US-EPA, contains no chlorine or bromine Non ozone depleting, low in toxocity, low in GWP, RoHS compliant and VOC exempt per US-EPA, contains no chlorine or bromine
Shelf life 4 years 2 years
Thickness <100 nm 0.1 - 1um
Tg 44°C 95°C
Thermal Stability of dry film Can withstand 175°C for 24h and maintain repellency Can withstand 175°C for 24h and maintain repellency
Contact angles WCA/OCA: 105°/65° WCA/OCA: 120°/80°
Refractive Index 1.39 1.376
Solder through repairability Yes Yes
Non-flammability Meets UL 94 V-0 Will meet UL 94 V-0 (Met via 5.5)
Dielectric Strength @ 35% RH 2000 V/mil 3600 V/mil
Cure None None
Application Anti stiction, Chemical protection, Corrosion protection, Moisture protection Anti stiction, Chemical protection, Corrosion protection, Moisture protection
Application location PCB, Electrical components PCB, Electrical components