  • Non conductive
  • Bondline thickness control
  • Black pigmentation

Product Description

LOCTITE 8387BS single component adhesive is designed for high throughput bonding applications. It contains spacers for improved bondline control.

LOCTITE 8387BS is a non conductive, black epoxy that blocks the stray light and has 30um polymer spacers to control the bondline thickness.

Cure Schedule

  • 1 hour @ 100°C 
  • 90 minutes @ 90°C
Product Family
10cc Syringe

Catalog Product

Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.
Not Available Shipping in 8 - 12 weeks

Technical Specifications

General Properties
Curing Schedule
Curing Schedule
Curing schedule is the time and temperature required for a mixed material to fully cure. While this applies to materials that cure with heat, there are also other materials that can be cured with UV.

Even though some materials can cure on ambient temperatures, others will require elevated temperature conditions to properly cure.

There are various curing schedules depending on the material type and application. For heat curing, the most common ones are Snap cure, Low temperature cure, Step cure and Staged cure.

Recommended cure type, schedule, time and temperature can always be found on the Technical data sheets.
Curing Heat Cure
Shelf Life
Shelf Life
Shelf life is the amount of time after manufacturing that a product is guaranteed to retain its properties.

It differs vastly per product and it is based on temperature and storage conditions.

The properties can be guaranteed for the temperature and time range indicated on the TDS since those are the ones tested to be the best for the product.
Shelf Life @ -40°C 365 days
Work life @25°C
Work life @25°C
Work life is the amount of time we have to work with a material until it is no longer able to be easily worked and applied on a substrate.

It is based on the change in viscosity and it can rely on the application requirements.
48 hours
Chemical Properties
Extractable Ionic Content, after 20 hours
Chloride (Cl-)
Chloride (Cl-)
The amount of Chloride (Cl-) ion extracted from the product in parts per million (ppm)
50 ppm
Potassium (K+)
Potassium (K+)
The amount of Potassium (K+) ion extracted from the product in parts per million (ppm)
10 ppm
Sodium (Na+)
Sodium (Na+)
The amount of Sodium (Na+) ion extracted from the product in parts per million (ppm)
10 ppm
Mechanical Properties
Die Shear Strength
Die Shear Strength
Die Shear Strength is the force that has to be applied to the side of the semiconductor die before it shears from its mounting.

Shear strength is measured for various die sizes, substrates and operating temperatures so check the Technical data sheet for your intended usage.
3x3mm @25°C 14 kg-f 
Tensile Modulus
Tensile Modulus
Tensile modulus is a mechanical property that measures the stiffness of an elastic material. It is the slope of stress / strain curve of a material under direct tensile loading.

It can be used to predict the elongation or elastic deformation of an object as long as the stress is less than the tensile strength of the material. Elastic deformation is caused by stretching the bonds between atoms and the deformation can be reversed when the load is removed.

Tensile modulus is affected by temperature and is an important engineering attribute since we generally want to keep elastic deformation as small as possible.
Tensile Modulus @-65°C 3,259 N/mm2
Tensile Modulus @100°C 790 N/mm2
Tensile Modulus @150°C 118 N/mm2
Tensile Modulus @25°C 1,919 N/mm2
Tensile Modulus @250°C 75 N/mm2
Viscosity is a measurement of a fluid’s resistance to flow.

Viscosity is commonly measured in centiPoise (cP). One cP is defined as
the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP.

A product like honey would have a much higher viscosity -around 10,000 cPs-
compared to water. As a result, honey would flow much slower out of a tipped glass than
water would.

The viscosity of a material can be decreased with an increase in temperature in
order to better suit an application
Thixotropic index
Thixotropic index
Thixotropic Index is a ratio of a material s viscosity at two different speeds in Ambient temperature, generally different by a factor of ten.

A thixotropic material s viscosity will decrease as agitation or pressure is increased. It indicates the capability of a material to hold its shape. Mayonnaise is a great example of this. It holds its shape very well, but when a shear stress is applied, the material easily spreads.

It helps in choosing a material in accordance to the application, dispense method and viscosity of a material.
Viscosity 14,250 mPa.s
Thermal Properties
Glass Transition Temperature (Tg)
Glass Transition Temperature (Tg)
The glass transition temperature for organic adhesives is a temperature region where the polymers change from glassy and brittle to soft and rubbery. Increasing the temperature further continues the softening process as the viscosity drops too. Temperatures between the glass transition temperature and below the decomposition point of the adhesive are the best region for bonding.

The glass-transition temperature Tg of a material characterizes the range of temperatures over which this glass transition occurs.
122 °C